 Preparation of Gold Semi-Nanoshell Arrays on Fiber Facet with Controllable LSPR Properties
作者:
 张腊梅12 廖艳林1 范群芳1 曹杰1 毛庆和1
 (1. 中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室, 合肥230031;
2. 郑州轻工业学院技术物理系, 郑州450002)
Author(s):
 ZHANG Lamei12 LIAO Yanlin1 FAN Qunfang1 CAO Jie1 MAO Qinghe1
 (1. Anhui Provincial Key Laboratory of Photonics Devices and Materials, Anhui Institute of Optics and Fine Mechanics,Chinese Academy of Sciences, Hefei 230031, China;
2. Department of Technology Physics, Zhengzhou University of Light Industry, Zhengzhou 450002, China)
关键词:
 光纤局域表面等离子体共振(LSPR)聚苯乙烯球(PS)单层膜金纳米半球壳阵列
Keywords:
 optical fiber localized surface plasmon resonance(LSPR) polystyrene sphere (PS) colloidal monolayer gold semi-nanoshell arrays
分类号:
-
DOI:
-
文献标识码:
A
摘要:
 提出了一种具有可调局域表面等离子体共振(LSPR)特性的光纤端面纳米结构的制备方法.利用二维胶体聚苯乙烯球(PS)单层膜的可转移性,结合溅射沉积,在光纤端面上获得了金纳米阵列结构.扫描电子显微镜和透射电子显微镜图像表明,单个纳米颗粒具有半球壳结构,阵列结构呈现六角密堆积排列;光谱测量结果显示,制备的样品具有明显的LSPR效应,改变溅射时间可实现对LSPR峰位从可见至近红外的调控,且金纳米半球壳直径改变时其LSPR峰位调控规律相似,重复测量结果表明制备的纳米结构具有良好的稳定性.
Abstract:
 A fabrication method of gold nanoparticale arrays on optical fiber facet with controllable localized surface plasmon resonance (LSPR) properties spectrum was presented in this paper. The gold nanoparticle arrays on fiber facet were fabricated based on the transferability of polystyrene sphere (PS) colloidal monolayer and the sputtering gold deposition on the PSs. The photos taken by both scanning and transmission electron microscopes show that, the single gold particle has a semi-nanoshell structure, and that the whole nanostructures on the fiber facet are in a hexagonally close-packed arrangement. Spectral analysis indicates that the gold nanoparticles on the fiber facet exhibit a remarkable LSPR effect, and that the LSPR peak location may be effectively controlled to move from the visible to near-infrared region by changing sputtering deposition time. A similar result can be obtained when the diameter of the gold semi-nanoshell is changed. Moreover, the measurement results also show that the LSPR properties of the fabricated nanostructure on fiber facet are very stable.